T10 SK105/SK95 1.1645 tool steel round steel bar
SHUNBEI
10 TON
Availability: | |||||||||
---|---|---|---|---|---|---|---|---|---|
Quantity: | |||||||||
T10 is the steel most commonly used for knife, because it is extremely hard and when properly forged provides great cutting power. | |||||||||
Product Description
T10 round bar application parameters
Product Name | T10 SK105/SK95 1.1645 tool steel round steel bar |
Length | 3m,6m,9m,12m or as required |
OD | 5.5mm~250mm or as required |
Standard | AISI,ASTM,DIN,JIS,GB,EN,etc |
Technique | Hot rolled (HR) or Cold rolled (CR) |
Thickness Tolerance | -0.05-0.07mm or 0.75-0.1mm or -1% |
MOQ | 1 ton. Sample order acceptable. |
Lead Time | Within 5-20days after receiving deposit. |
Export packing | Waterproof paper protected, steel strip packed stably, and fixed well.Standard Export Seaworthy Package. Suit for all kinds of transportation means; or as required |
T10 round bar Chemical Composition:
Element | Composition (%) |
Carbon (C) | 0.95-1.04 |
Silicon (Si) | ≤0.35 |
Manganese (Mn) | ≤0.40 |
Phosphorus (P) | ≤0.035 |
Sulfur (S) | ≤0.030 |
Chromium (Cr) | ≤0.25 |
Nickel (Ni) | ≤0.20 |
Copper (Cu) | ≤0.25 |
Product Description
T10 is a kind of carbon tool steel, which is mainly composed of iron and carbon, and sometimes a small amount of other elements, such as 1.5% manganese, can be added to improve its strength. In addition, there are T8 and T9 steels. Compared with T10, its strength and wear resistance have been improved, but the hot hardness is slightly lower. After quenching and heating, it is not easy to overheat, and always maintains the crystal structure, but after quenching, its wear resistance can be improved. Relatively speaking, the production cost is slightly lower, and the scope of application is relatively wide. For example, making super knives or drill bits, or making some molds, etc., can use this kind of steel.
Application
Ordinary carbon structural steel has a wide range of applications. Generally used as building materials and less important mechanical parts, making screws, anchor screws, furnace parts, agricultural machinery, building structures, rolled into I-beams, channel steels, angle steels, steel plates, steel pipes and other various Profiles, manufacturing various parts, can also be heat treated.