38CrMoAl Alloy sheet
SHUNBEI
10 TON
| Quantity: | |||||||||
|---|---|---|---|---|---|---|---|---|---|
| 38CrMoAl is a nitrided Alloy Steel with high wear resistance, high fatigue strength and high strength. | |||||||||
Product Description
38CrMoAl steel application parameters:
| Product Name | Stock Available GB 38CrMoAl JIS SACM645 Engineering Steel Hot Rolled Steel |
| Length | Coils are in rolls packing, bigger rolls, smaller rolls acceptable; As required. |
| Width | 1250 or 1530mm |
| 1219 or 1500mm (Slit Edges) | |
| Narrow width is Strips, if you need, pls just contact us for more. | |
| Thickness | 0.2mm-5mm (CR); 2.7-100mm (HR) or as required |
| Standard | AISI,ASTM,DIN,JIS,GB,EN,etc. ; |
| Technique | Hot rolled (HR) or Cold rolled (CR) |
| Thickness Tolerance | -0.05-0.07mm or 0.75-0.1mm or -1% |
| Main Grades | 10# 20# 35# 45# 50# 60# Q345B Q345C Q345D Q345E,Q235B Q235R Q355B ST12 ST37 ST52 etc. |
38CrMoAl Steel Chemical Composition:
Element | Composition (%) |
C | 0.35～0.42 |
Si | 0.20～0.45 |
Mn | 0.30～0.60 |
S | ≤0.035 |
P | ≤0.035 |
Cr | 1.35～1.65 |
| AI | 0.70～1.10 |
| Ni | ≤0.30 |
| Cu | ≤0.30 |
Mo | 0.40~0.55 |
Product Description
38CrMoAl is a high-grade nitriding steel. On the basis of ordinary carbon Bai plain steel, nitrogen atoms are infiltrated into the surface layer of the workpiece in a certain medium at a certain temperature, so as to obtain the characteristics of high wear resistance, high fatigue strength, high strength, corrosion resistance and high temperature resistance.
Application
It is mainly used for nitriding parts with accurate size after heat treatment, or various nitriding parts with low impact load and high wear resistance, such as mould imitation, cylinder liner, gear, high pressure valve, boring bar, worm, grinder spindle, etc., but the parts with larger size should not be used.